合成气洗涤塔闪爆损坏机理研究(含CAD图)

合成气洗涤塔闪爆损坏机理研究(含CAD图)(任务书,外文翻译,论文14000字,CAD图2张)
摘要
本文针对惠生（南京）化工有限公司T1301合成气洗涤塔经历一次意外的闪爆后，出现沿（部分）接管与筒体的角焊缝开裂、封头变形以及筒体周向变形等破坏进行分析，其筒体材质为16Mn+内衬不锈钢，本文主要结合内衬不锈钢304材料性能，利用有限元法对合成气洗涤塔进行应力分析，从而对筒体的损坏机理研究，提出相关方面的修复方案和建议。
关键词：失效分析  接管  裂纹  内衬不锈钢304

The Mechanism of Syngas Scrubber Explosion Damage
Abstract
In this paper, HuiSheng( Nanjing )chemical Ltd. T1301 syngas scrubber experienced an unexpected flash explosion , there was along the ( partial ) over the fillet weld cracking and the cylinder , cylinder head deformation and destruction carried circumferential deformation analysis, the cylinder is made of 16Mn + lined with stainless steel , this paper combines lined with stainless steel 304 material properties, using the finite element method for the synthesis gas scrubber stress analysis , and thus the mechanism of damage to the cylinder , make relevant aspects of the rehabilitation program and recommendations.
Keywords: failure analysis；cylinder；crack；Lined with stainless steel 304
 

目录
摘要    Ⅰ
ABSTRACT    Ⅱ
第一章  绪论    1
1.1 研究背景    1
1.2研究意义    4
第二章 失效分析    5
2.1 失效和失效分析    5
2.1.1 失效    6
2.1.2 失效分析    8
2.1.3 失效分析在工程中的地位和作用    10
2.2金属的力学性能    12
2.2.1金属的塑性变形    13
2.2.2合金    15
2.2.3铁碳合金相变基础理论    16
第三章 不锈钢304    19
3.1不锈钢内衬    19
3.2 不锈钢304基本信息    19
3.3 不锈钢304分类及性能特点    21
3.4 不锈钢304的力学性能及机械性能    21
3.6 不锈钢304的耐腐蚀性能    24
3.7 不锈钢304的焊接性    24
第四章 裂纹失效分析    25
4.1 强度分析    25
4.1.1 内压圆筒校核    25
4.1.2 开孔补强计算    26
4.2 应力分析    28
4.2.1概述    28
4.2.2应力计算参数    28
4.2.3 强度评定    29
4.2.5结论    30
第五章 结论与修复方案及建议    30
5.1 T1301洗涤塔闪爆后的损坏机理    30
5.2闪爆后破坏程度的测量    31
5.3损伤缺陷的修复和评价    32
5.4建议    32
参考文献    33